Zinc oxide is widely used in rubber, paint, ceramics, chemical, pharmaceutical, glass and electronics industries. With the rapid development of industry, the domestic demand for zinc oxide is increasing. The use of low-grade zinc-containing materials to produce active zinc oxide not only makes full use of zinc resources, but also reduces production costs. Therefore, the research field is currently very active, comprehensively utilizing low-grade oxidized ore, sub-oxidized ore, zinc slag, soot, etc. Research has gradually attracted the attention of enterprises. Soot lead, an intermediate product of metallurgical processes zinc is volatilized from the rotary kiln, depleted of zinc lead blast furnace slag and other materials generated by its complex composition, in addition to zinc, also contain lead more arsenic, 锑 and other impurities. Due to its difficulty in processing and high cost, it cannot be directly used as a raw material for wet zinc smelting. However, since it has a high zinc content and is easily leached into a human solution, it can be used as a zinc oxide powder product.
The existing methods for treating soot are acid leaching method and ammonia compounding method. The acid leaching method uses zinc oxide or zinc ore as raw material, and reacts with dilute acid to obtain zinc oxide by impurity removal, neutralization, drying and calcination. The method has large impurity removal, complicated process, high cost, large amount of waste water, difficult treatment and pollution to the environment. The ammonia compounding method is a process of using zinc oxide or desulfurized zinc catalyst calcined material as raw material, ammonia water-ammonium bicarbonate solution as leaching agent, leaching, decontamination purification, steaming ammonia zirconium, washing and drying, and calcination. Active zinc oxide is produced. The method has less investment in equipment and less impurities, but the process is long, and it is only suitable for materials rich in ZnO. If the material contains a certain amount of ZnS, the method cannot be directly used, and the oxidant is used to pre-treat the soot and zinc sulfide. Converted to zinc oxide. Therefore, it has been experimentally studied to pretreat soot with hydrogen peroxide and then leaching with sodium hydroxide solution to obtain a zinc oxide powder product.
First, the test part
(1) Test materials
The test soot was taken from a factory in Guangxi with a particle size of 65-76 μm. The main chemical compositions are shown in Table 1.
Table 1 Chemical composition of soot
Zn | Pb | Fe | As | Cd | Sb | Si | S |
49.86 | 26.89 | 0.75 | 0.80 | 0.03 | 0.11 | 0.5 | 1.81 |
(2) Test methods
Firstly, the dry soot is prepared into a soot slurry with a liquid solid mass ratio of 1:1, and then pretreated with 3% hydrogen peroxide for a certain period of time, and then added with a certain amount of sodium hydroxide solution at a certain temperature, stirred and leached, and then centrifuged to filtrate. After appropriate dilution and stirring for a period of time, the mixture is centrifuged again, and the secondary filtrate is returned as a leaching agent, and the filter cake is zinc hydroxide. After washing, drying and calcining, pure zinc oxide powder is obtained.
Second, the results and discussion
(1) Effect of volume fraction of hydrogen peroxide and pretreatment temperature on zinc leaching rate
At different temperatures, add a certain amount of hydrogen peroxide to 100g of soot slurry (liquid solid mass ratio 1:1), stir for 60min, and then immerse in 3mol/L sodium hydroxide solution for 2h at 60°C to observe the volume fraction of hydrogen peroxide. And the effect of pretreatment temperature on zinc leaching rate in soot, the results are shown in Table 2.
Table 2 Effect of volume fraction of hydrogen peroxide and pretreatment temperature on zinc leaching rate
Test number | Hydrogen peroxide volume fraction /% | Pretreatment temperature / °C | Zinc leaching rate /% |
1 | 1 | 25 | 38.24 |
2 | 3 | 25 | 55.67 |
3 | 5 | 25 | 56.71 |
4 | 1 | 40 | 40.33 |
5 | 3 | 40 | 60.01 |
6 | 5 | 40 | 61.24 |
It can be seen from Table 2 that the volume fraction of hydrogen peroxide increases and the leaching rate of zinc increases. At 25 °C, when the volume fraction of hydrogen peroxide increases from 1% to 3%, the zinc leaching rate increases by 17%; the volume fraction of hydrogen peroxide is from 3%. When the temperature is increased to 5%, the zinc leaching rate is only increased by 1%; when the temperature is raised to 40 °C, the volume fraction of hydrogen peroxide is increased from 1% to 3%, the zinc leaching rate is increased by nearly 20%, and the SO of zinc oxide is adsorbed. 2 is oxidized by hydrogen peroxide to zinc sulfate, which does not pollute the environment. It can be considered that the temperature has little effect on the zinc leaching rate, and the volume fraction of hydrogen peroxide is 3%.
(2) Effect of temperature on zinc leaching rate
The soot was pretreated with 3% hydrogen peroxide at 25 ° C, and then leached with a 3 mol/L sodium hydroxide solution at different temperatures for 1.5 h. The test results are shown in Figure 1.
Fig.1 The leaching temperature on the rate of zinc diffusion in soot
It can be seen from Figure 1 that as the leaching temperature increases, the zinc leaching rate increases linearly. At room temperature, the zinc leaching rate is only 30.22%, and when the temperature is raised to 95 °C, the zinc leaching rate reaches 89.31%. Considering comprehensively, the leaching temperature is preferably 85 °C.
(3) The effect of sodium hydroxide concentration on zinc leaching rate
The soot was pretreated with 3% hydrogen peroxide at 25 ° C and then leached with different concentrations of sodium hydroxide solution at 85 ° C for 1.5 h. The test results are shown in Figure 2.
Figure 2 Effect of sodium hydroxide concentration on zinc leaching rate
It can be seen from Fig. 2 that as the concentration of sodium hydroxide increases, the zinc leaching rate increases, especially the concentration of sodium hydroxide increases from 2 mol/L to 5 mol/L, and the zinc leaching rate increases by 46.54% to 97%. This is due to the reaction of zinc and alkali in the soot to form sodium zincate into the solution:
2 NaOH + ZnO = Na 2 ZnO 2 + H 2 O.
However, when the concentration of sodium hydroxide is increased to 6 mol/L, the zinc leaching rate is only increased by 0.52%, which cannot reach 100%. This may be because the zinc in the soot is wrapped and cannot be contacted with the alkali.
(4) Effect of leaching time on zinc leaching rate
The soot was pretreated with 3% hydrogen peroxide at 25 ° C, and then leached with a 3 mol/L sodium hydroxide solution at 85 ° C to investigate the effect of leaching time on zinc leaching rate. The result is shown in Figure 3.
Figure 3 Effect of leaching time on zinc leaching rate
It can be seen from Fig. 3 that as the reaction time increases, the zinc leaching rate increases. After leaching for 0.5 to 1.5 hours, the zinc leaching rate increased from 73.81% to 96.92%; however, after 1.5 hours of leaching, the zinc leaching rate increased slowly. Therefore, the leaching time is preferably 1.5h.
(5) Verification test
The soot was pretreated with 3% hydrogen peroxide at 25 ° C, and then leached with a 5 mol / L sodium hydroxide solution at 85 ° C for 1.5 h.
The zinc leaching rate and the mass fraction of zinc and lead in the leaching slag are shown in Table 3.
Table 3 Test results of alkali leaching soot verification test
Test number | Zinc leaching rate /% | ωB/% in leaching residue |
Zn | Pb | As |
1 | 96.92 | 3.91 | 45.33 | 0.02 |
2 | 97.03 | 3.42 | 45.20 | <0.01 |
3 | 96.98 | 4.01 | 45.28 | 0.01 |
4 | 97.13 | 3.66 | 46.21 | <0.01 |
It can be seen from Table 3 that under the comprehensive test conditions, the zinc leaching rate is about 97%, the zinc content in the leaching slag is between 3% and 4%, and the lead mass fraction is about 45%, which contains almost no As. Leaching slag can enter the lead system to extract lead and realize comprehensive utilization of resources.
(6) Preparation of zinc oxide
The alkali leaching solution was cooled to 25 ° C, diluted 1 time, stirred for 0.5 h, then centrifuged, and the filter cake was dried, and the zinc hydroxide precipitation rate was 72.3%. The XRD analysis of the precipitate showed that the phase composition was mainly ZnO. The chemical analysis showed that the mass fraction of ZnO was 99.58% and the mass fraction of Pb0 was 0.12%, which basically met the requirements of the direct method.
Third, the conclusion
The zinc-containing soot is pre-oxidized by hydrogen peroxide at room temperature and then leached with sodium hydroxide solution, 97% of the zinc can be transferred into the solution, and then precipitated, filtered and dried to obtain zinc oxide powder. The purity of the ZnO powder obtained by the method is high, which provides an effective way to make full use of the zinc-containing soot.
Bonding Metal Powder Coating
Bonding metal powder coating
We utilize advanced metal bonding techniques to give our products excellent batch stability and a metallic texture. Simultaneously, with our mature formulation system, we can achieve various texture effects in coatings. Rainbow Beauty metallic powder coatings are widely used in many fields such as household appliances, aluminum profiles, doors and windows, engineering construction, fitness equipment, transportation, and more.
PROPERTIES
Control the chromatc aberration Magnificent metal twinkle effect strong omament.
among different batches effectively.
Non-toxic and safe:food grade. Good in mechanical and physical properties.
OPERATING PARAMETERS
l Pre-treatment
|
Pre-treatment
|
|
Pre-treatment
|
Degreasing, rust removal, sandblasting, phosphating, silane treatment, or ceramic coating, etc.
|
|
Attention
|
Before spraying, please ensure that the substrate is thoroughly degreased and rust-free, with no impurities, water stains, or residual liquid.
|
|
Note
|
Acid washing and sandblasting the substrate can enhance the adhesion between the coating and the substrate.
|
Spraying requirements
Cured condtions：15 mins. at 180℃ metal temperature Cured Film Thickness：80um.
Storage Stability
Keep storage environment well-ventilated and dry, with temperatures not exceeding 27°C.
Properties parameter
|
Items
|
Standard
|
Result
|
|
Impact
|
ASTM D-2794
|
80in.ibf（Direct)/20in.ibf（indirect)
|
|
Pencil Hardness
|
ASTM D3363
|
≧2H
|
|
Adhesion(100cells)
|
ASTM D-3359
|
Full pass (5B)
|
|
Flexibility
|
ASTM D522
|
3/16'inch
|
|
Salt spray resistance(5%Nacl)
|
ASTM B-117
|
1500H,Corrsion,≤3mm,
|
|
QUV Resistance(UV340)
|
ASTM G-154
|
1500H ΔE≤4
|
Why choose Holyme?
Bonding metal powder coating
HLM Powder Coating CO,.Ltd , https://www.holymepowder.com